Mr NelsonWe met Lily from friction material Fair in Shanghai. She is very professional with friction and sealing materials. We imported brake lining and gasket joint sheets from Xinyan factory for 4 years. A good and pleasant cooperation all the time. Very honest supplier, we trust them and believe you also could make beneficial cooperation with Xinyan comp
150 Degree 4.0Mpa Resin Anchor Windlass Brake Lining
|Product Name||Woven Brake Lining With Resin||Product Color||Brown|
|Application||Anchor||Size||10, 15, 20 Meters/roll|
|Material||Brass Wire, Resin, Viscose,||Type||BXS-M|
resin anchor windlass brake lining,
4.0Mpa anchor windlass brake lining,
dock crane brake lining
Non Asbestos Woven Brake Lining yellow anchor brake lining
Model: BXS-M Non-asbestos Woven Brake Lining
Material: Viscose fiber, Aramid fiber, glass fiber, 2 brass wires, Melamine resin.
Working Conditions: 250℃,Static Pressure: 4.0Mpa
Applied field: It is widely used for braking deceleration and transmitting power of big power machineries.
Specification: T(5~30)x W(≤500)mm ; Available Length: 10m,15m,20m
Non-asbestos Woven Brake Lining selects new-type abrasion resistant and high temperature resistant non-asbestos yarns which contain brass wires, viscose fiber, Glass fiber, Aramid fiber etc.
Our product owns high performance of wear resistance, low wear rate, high tensile strength, good softness, high temperature resistance, corrosion resistance, oil resistance, long service life and impact resistance etc. They are definitely 100% non-toxic, pollution free and environmental products.
It is widely used for braking deceleration and transmitting power of big power machinery, such as ship winch, dock crane, drilling machinery, lifting machine, building machinery etc.
|Temperature||Coefficient of friction(μ)||Wear rate(v)(cm³/N.m)|
|100℃||0.35~0.65||≤0.7 x 10-7|
|150℃||0.35~0.65||≤1.1 x 10-7|
|200℃||0.30~0.60||≤1.5 x 10-7|
|250℃||0.25~0.60||≤2.5 x 10-7|
We adopt Japanese Technology. All yarns are woven by advanced Japanese loom machinery & equipment then impregnate into specially formulated polymer resin, through high temperature, low temperature etc. processing workmanship.